MobilityMiniaturization and Light Weight
Achieved process reduction and structural freedom through phenolic resin molding,
contributing to the miniaturization and weight reduction of metal substitute parts.
Achieved process reduction and structural freedom through phenolic resin molding,
contributing to the miniaturization and weight reduction of metal substitute parts.
Grade | PM-5245 | PM-5265 (Development material) |
PM-9640 | |
---|---|---|---|---|
Characteristic | Dimensional stability | High dimensional accuracy Low specific gravity |
GF reinforced | |
Specific gravity | - | 2.03 | 1.90 | 1.78 |
Molding Shrinkage | % | 0.24 | 0.30 | 0.28 |
CTE (MD/TD) | ppm/K | 13/14 | 16/18 | 14/30 |
Flexural strength | MPa | 180 | 180 | 225 |
Flexural modulus | GPa | 23 | 18 | 16 |
Tensile strength | MPa | 110 | 110 | 140 |
Compressive strength | MPa | 360 | 340 | 320 |
Charpy Impact strength | kJ/m2 | 3.0 | 3.0 | 5.2 |