High heat resistance and high insulation thermosetting resin
improves functionality and reliability of electric power train.
High heat resistance and high insulation thermosetting resin
improves functionality and reliability of electric power train.
Test items | Conditions | Unit | ALC-1371 (120µm) |
ALC-1331 (80µm) |
Thermal Conductivity(LF) | A | W/m·K | 7 | 3 |
Breakdown Voltage DC | A | kV | >10 | >10 |
Breakdown Voltage AC | A | kV | 6 | 6 |
Peel Strength (35μm) | A | N/mm | 1.7 | 1.5 |
Flammability | UL94(A) | - | 94V-0 | 94V-0 |
Tracking Resistance | A (IEC method) |
V | 600 | 600 |
Tg | TMA | deg.C | 130 | 100 |
Young’s Modulus | A | GPa | 40 | 21 |
Water Absorption | D-24/23 | % | 0.3 | 0.3 |
Chemical Resistance | 3%NeOH 40deg.C 3min |
- | OK | OK |
---|
* The data table shown are representative values, not guaranteed values.
Test items | Conditions | CLC-5201 (175µm) |
|
Thermal Conductivity | w/m・K | Laser flash / 25°C | >12 |
---|---|---|---|
w/m・K | Laser flash / 175°C | >10 | |
Breakdown Voltage | kVrms | AC / 25℃ | >8 |
Volume Resistivity | Ω・cm | DC, 1 kV, 1 min / 25°C | 1E+16 |
Ω・cm | DC, 1 kV, 1 min/ 175°C | 1E+13 | |
Dielectric Constant | ― | 1MHz | 4.6 |
Tg | ℃ | TMA | >200 |
* The data table shown are representative values, not guaranteed values.